3004 Aluminum Coil Alloy Aluminum 3004 Mill Finish 3004 H32 H34
Properties of 3004 Aluminum Coil:
3004 aluminum alloy is an alloy in the wrought aluminum-manganese family (3000 or 3xxx series). It is similar to the 3003 alloys, except for the addition of approximately 1% magnesium. It can be cold worked (but not, unlike some other types of aluminum alloys, heat-treated) to produce tempers with higher strength, but a lower ductility. Like most other aluminum-manganese alloys, 3004 is a general-purpose alloy with moderate strength, good workability, and good corrosion resistance. It is commonly rolled and extruded (used in the making of beverage cans), but typically not forged. As a wrought alloy, it is not used in casting.
Chemical Composition of 3004 Aluminum Coil (%):
| Elements | Si | Cu | Mg | Zn | Mn | Fe | Al |
| Contents | 0.3 | 0.25 | 0.8-1.3 | 0.25 | 1.0-1.5 | 0.7 | remainder |
Mechanical Properties of 3004 Aluminum Coil:
| Temper | Ultimate Tensile Strength | Ultimate Yield Strength | Shear Strength | Elongation | Hardness |
| 3004-O | 180 MPa/26 Ksi | 69 MPa/10 Ksi | 110 MPa/16 Ksi | 20-25 % | 45 HB |
| 3004-H34 | 215 MPa/31 Ksi | 170 MPa/25 Ksi | 115 MPa/17 Ksi | 10-17 % | 52 HB |
| 3004-H36 | 240 MPa/35 Ksi | 200 MPa/25 Ksi | 125 MPa/18 Ksi | 9-12 % | 63 HB |
| 3004-H36 | 260 MPa/38 Ksi | 230 MPa/33 Ksi | 140 MPa/20 Ksi | 5-9 % | 70 HB |
| 3004-H38 | 285 MPa/41 Ksi | 250 MPa/36 Ksi | 145 MPa/21 Ksi | 4-6 % | 77 HB |
Applications of 3004 Aluminium Coil:
1. 3004 aluminum coil mainly used for processing the component parts that need to have good formability, high solderability good resistance to corrosion, such as kitchen utensils and appliances, food and chemical products processing and storage devices, transport tank, a tank of liquid products.
2. 3004 aluminum coil mainly used in chemical production and storage equipment, plate processing, building materials, construction, cable pipes, sewer pipes, various parts of lamps and lanterns, cans, wave plate, building materials, color aluminum plate, electric light head.
3. 3004 aluminum sheet mainly used in processing pressure vessel, pipeline, utensil, cooling fin, radiator, makeup board, copy machine roller, ship material.
Informations of 3004 Aluminum Coil:
1-A: What's the difference between 3003 Aluminum Coil and 3004 Aluminum Coil?
These two general purpose alloys are very similar. In terms of their chemical composition, 3004 aluminum has an addition of magnesium which gives this grade the upper hand when it comes to strength.
1-B: Is 3004 aluminum used for cookware?
Yes, this grade is commonly used in kitchen and cookware manufacturing.
1-C: What are 3004 uses?
It has many uses due to good strength, excellent corrosion resistance, good formability, good workability and drawing characteristics. This includes beverage cans, chemical equipment, hardware, storage tanks, and lamp bases. Because it is so similar to 3003, it will be seen in similar applications, and especially those requiring higher strength.
Our Services:
1. Reply within 12 hours;
2. Free samples provided;
3. On-site production following-up;
4. Loading inspection with container fixing;
5. Third party inspection at your request;
6. Every employee of our company is the most professional and does their best to provide you with quality service.
Product Tags:
|
|
3004 Mill Finish Aluminum Coil Sheet H32 H34 Thick 0.3mm To 20mm Images
|